This study covers an investigation on welding high strength armor steels with austenitic filler material using Gas Metal Arc Welding process. Armor plates conforming to MIL A 46100 standard were prepared with six different groove angles using 307 Si austenitic stainless steel electrode. Welded test specimens were subjected to tensile testing and microhardness measurements in three zones (fusion zone, heat affected zone and base metal zone) were recorded. Comparing the results obtained from both tensile testing and microhardness measurements, the optimum groove angle to result in the highest mechanical properties is determined.
Özet
Bu çalışmada, yüksek sertlikli zırh çeliği östenik paslanmaz çelik elektrot kullanılarak MIG (Metal Inert Gas) yöntemiyle kaynak edilmiştir. MIL A 46100 zrh çeliğinden, 6 farklı açıda plakalar hazırlanmış ve 307Si östenitik paslanmaz çelik elektrot kullanılarak kaynak edilmiştir. Hazırlanan bu numunelere çekme deneyi ve 3 bölgeyi kapsayacak şekilde (kaynak metali, ısı tesiri altında kalan bölge, esas metal bölgesi) mikro sertlik taraması yapılmıştır. Elde edilen sonuçlar karşılıklı olarak değerlendirilerek en uygun kaynak açısı belirlenmiştir.