AI InsightAccording to the results obtained, it was observed that with the increase of the amount of glass fiber in the mixture, there were decreases in the workability, compressive strength and ultrasonic pulse velocity of the mixture and improvements in the flexural strength in general.
📌 3 Key Takeaways
Abstract
Different fiber types are used in concrete production in order to make improvements in the engineering properties of concrete. However, properties such as the type of fibers and the slenderness have different effects on the properties of the concrete to be produced. In this study, glass fibers of 3 mm, 6 mm and 12 mm in length were added to mixtures of 0.3%, 0.4% and 0.5% by volume, and the workability, compressive strength, flexural strength and ultrasonic pulse velocity of the produced mortars were investigated. According to the results obtained, it was observed that with the increase of the amount of glass fiber in the mixture, there were decreases in the workability, compressive strength and ultrasonic pulse velocity of the mixture and improvements in the flexural strength in general.
Özet
Betonun mühendislik özelliklerinde iyileştirmeler yapabilmek için farklı lif türleri beton üretiminde kullanılmaktadır. Fakat lif türü, narinlik gibi değişkenler üretilecek olan betonun özellikleri üzerinde farklı etkilere sahiptir. Bu çalışma kapsamında, farklı uzunluklardaki (3 mm, 6 mm ve 12 mm) cam lifleri, karışıma hacimce % 0.3, % 0.4 ve % 0.5 oranlarında ilave edilerek üretilen harçların yayılma değeri, basınç dayanımı, eğilmede çekme dayanımı ve ultrasonik atımlı dalga hızı incelendi. Elde edilen sonuçlara göre, karışım içerisindeki cam lif miktarının artmasıyla genel olarak karışımın yayılma değerinde, basınç dayanımı ve ultrasonik atımlı dalga hızında azalmalar meydana gelirken, eğilmede çekme dayanımında ise iyileşmeler meydana geldiği görülmüştür.