AI InsightTest results indicated that the use of excessive dosages of chemical admixtures significantly decreased compressive strength of concretes and extended demoulding time.
📌 3 Key Takeaways
Abstract
In this study, the effect of the use of excessive dosages of normal and superplasticizer admixtures on the compressive strength and absorption properties of concrete was investigated. Normal plasticizer admixtures were used 0.5 %, 1 %, 5 % and 10 % by weight of cement and superplasticizer admixtures were used 1.5 %, 3 %, 5 % and % 10 by weight of cement. Unit weight and slump tests were conducted on the fresh concretes and compressive strenght and water absorption tests were conducted on the hardened concrete samples. Test results indicated that the use of excessive dosages of chemical admixtures significantly decreased compressive strength of concretes and extended demoulding time. Moreover, the best plasticizer proportion range was found 1 % - 1.5 %. Furthermore, water absorption values were obtained in the range of 1.95 % - 5.65 %.
Özet
Bu çalışmada, 300 ve 450 dozajlı betonlarda aşırı dozda normal ve süper akışkanlaştırıcı katkı kullanımının beton basınç dayanımına, su emme yüzdesine etkisi araştırılmıştır. Katkı miktarları normal akışkanlaştırıcı (NA) katkılarda % 0.5, % 1, % 5 ve % 10, süper akışkanlaştırıcı (SA) katkılarda ise % 1.5, % 3, % 5 ve % 10 oranlarında kullanılmıştır. Üretilen bu betonlar üzerinde taze halde iken birim ağırlık ve çökme deneyleri, sertleşmiş halde iken basınç dayanımı ve su emme deneyi yapılmıştır. Deney sonuçlarına göre aşırı dozda katkı kullanımının beton basınç dayanımını ciddi oranda düşürdüğü ve kalıp alma süresini uzattığı görülmüştür. Basınç dayanımı olarak en ideal katkı yüzdesinin % 1 - % 1.5 arasında olduğu anlaşılmıştır. Sertleşmiş betonların su emme yüzdesi oranlarının % 1.95 - % 5.65 aralığında olduğu görülmüştür.