AI InsightThe ferromagnetic order in the Cu1 - xCox films was between 2.5-29%.
📌 3 Key Takeaways
Abstract
The magnetic properties of Cu1 - xCox alloy films prepared by electrodeposition technique were investigated by Alternating Gradient Force Magnetometer. The magnetization curves of Cu0.94Co0.06, Cu0.87Co0.13 and Cu0.74Co0.26 films were easily saturated while the other Cu1 - xCox samples with x= 0.17, 0.19 and 0.21 had more inclined magnetization curves. The saturation magnetization value of Cu1 - xCox film increased with increasing Co content in the film. The minimum values of the ratio of remanence to magnetization and the coercive field were determined in the Cu0.81Co0.19 alloy film among the others. The ferromagnetic order in the Cu1 - xCox films was between 2.5-29%.
Özet
The magnetic properties of Cu1 - xCox alloy films prepared by electrodeposition technique were investigated by Alternating Gradient Force Magnetometer. The magnetization curves of Cu0.94Co0.06, Cu0.87Co0.13 and Cu0.74Co0.26 films were easily saturated while the other Cu1 - xCox samples with x= 0.17, 0.19 and 0.21 had more inclined magnetization curves. The saturation magnetization value of Cu1 - xCox film increased with increasing Co content in the film. The minimum values of the ratio of remanence to magnetization and the coercive field were determined in the Cu0.81Co0.19 alloy film among the others. The ferromagnetic order in the Cu1 - xCox films was between 2.5-29%.