In this work, the effect of temperature and crosshead speed on dynamic strain ageing were investigated for as-received and heat treated samples of vanadium microalloyed steel. All samples were tested at 200°C and 350°C by using two crosshead speeds of 0.5 and 2 mm/min. It was observed that increasing temperature has the same effect on increasing workhardening rate as reducing crosshead displacement rate suggesting the onset of dynamic strain ageing.
Özet
Bu çalışmada, sıcaklık ve çekme hızının ısıl işlem görmüş ve görmemiş durumlardaki vanadyum içeren mikroalaşımlı çelik üzerindeki etkisi incelendi. Bütün deneyler 200°C ve 350°C sıcaklıklarda ve 0.5 ve 2 mm/dak.' lık çekme hızlarında gerçekleştirildi. Deney sıcaklığının yükselmesinin, çekme hızının düşmesi ve deformasyon sertleşmesinin artmasıyla aynı etkiyi gösterdiği görüldü. Bu durum dinamik yaşlandırma sertleşmesinin vanadyumlu mikroalaşım çeliklerinde belirtilen koşullarda meydana geldiğini göstermektedir.