Investigation of Engineering Properties of Blast Furnace Slag Additive Mortars

Osman Gunaydın
Kadir Güçlüer
Hüseyin Boran
Pages
138–143
Publication Date
2022-10-19
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

The highest freeze-thaw resisting value was seen in the sample with 30% BFS with 1.35%.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:Cement, water and fine aggregate mixture is called mortar.
📊
Key Findings & Data:In this study, instead of standard sand, blast furnace slag (BFS) was used at 10%, 20% and 30% by weight in mortar samples.
💡
Conclusion & Impact:The highest freeze-thaw resisting value was seen in the sample with 30% BFS with 1.35%.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Mortar · Blast Furnace Slag · Electrical Resistivity

Abstract

Cement, water and fine aggregate mixture is called mortar. Mortar samples suitable for the desired purpose can be obtained by adding various additives to the mortar samples. In this study, instead of standard sand, blast furnace slag (BFS) was used at 10%, 20% and 30% by weight in mortar samples. In order to determine the mechanical properties of the samples, compressive and flexural strength tests were applied. For the electrical resistivity values, a device with constant 30V voltage was prepared and the electrical resistivity values were measured. To determine the freeze-thaw resisting properties, it was applied sodium sulfate experiment. As a result, it was seen that the best values were obtained from 30% BFS additive samples in all series. The highest resistivity values are in the sample with 30% BFS doped with 0.1856 ohm.m and 0.268 ohm.m values. The highest freeze-thaw resisting value was seen in the sample with 30% BFS with 1.35%.

🔖

Cite This Article

Gunaydın, O., Güçlüer, K., Boran, H. (2022). Investigation of Engineering Properties of Blast Furnace Slag Additive Mortars. Manas Journal of Engineering, Cilt: 8 - Sayı: 2, 138–143. https://ajindex.com/articles/578024

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (17)

  1. Baradan B., Yazıcı H. ve Aydın S., Beton. Dokuz Eylül Üniversitesi Mühendislik Fakültesi Yayınları, İzmir: 2015
  2. Jadhav, P.A. ve Kulkarni, D.K., ‘‘Effect of Replacement of Natural Sand By Manufactured Sand on the Properties of Cement Mortar,’’ International Journal of Advanced Engineering Technology, Vol. 3, No 3, (2013)
  3. Hiraskar, K.G. ve Patil, C. ‘‘Use of Blast Furnace Slag Aggregate in Concrete,’’ International Journal Of Scientific & Engineering Research, Volume 4, Issue 5, (2013), s 95
  4. Thomas D., Concrete Durability. CRC Press, 2014
  5. Babu K. D. and Kumar V. S. R., “Efficiency of GGBS in Concrete”, Cement and Concrete Research, 30, (2000), 1031- 1036
  6. Erdoğan T. Y., Beton. Metu Press, 5. Baskı, 2015
  7. Babu K. D. and Kumar V. S. R., “Efficiency of GGBS in Concrete”, Cement and Concrete Research, 30, (2000), 1031- 1036
  8. Salem T.M., “Electrical conductivity and rheological properties of ordinary portland cement–silica fume and calcium hydroxide–silica fume pastes”, Cem Concr Res, 32, (2002), 1473-1481
  9. McCarter W.J., Starrs G. and Chrisp T.M., Electrical conductivity, diffusion, and permeability of portland cement-based mortars, Cem Concr Res, 30, (2000), 1395-1400
  10. Topçu İ. B., Uygunoğlu T. ve Hocaoğlu İ., “Yüksek fırın cüruf katkılı çimento pastalarının elektriksel özdirençlerinin araştırılması”, Politeknik Dergisi, 21(2), (2018), 257-264
  11. Binici H. et al, ‘‘Kum Boyutunda Yüksek Fırın Cürufu ve Pomza Katkılı Beton Boruların Durabilite Özelliklerinin Araştırılması’’, Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, 14.3, (2012), 33-44
  12. Nataraja, M.C., Kumar, D.P.G., Manu, A.S. ve Sanjay, M.C., ‘‘Use Of Granulated Blast Furnace Slag As Fine Aggregate In Cement Mortar,’’ International Jounal of Structural and Civil Engineering Research. No.2, May, (2013)
  13. Babu, J.S. ve Mahendran, N., ‘‘Experimental Studies on Concrete Replacing Fine Aggregate with Blast Furnace Slags,’’ International Journal of Engineering Trends and Technology (IJETT). Volume 10, Number 8, Apr, (2014)
  14. Autade, P. B., & Saluja, H. S. J. S. Effect of Steel Slag as a Replacement of Fine Aggregate in M40 Grade of Concrete, 2016
  15. Şeker, O., ‘‘Granüle Yüksek Fırın Cürufunun Kendiliğinden Yerleşen Beton Özelliklerine Etkisi,’’ Master's thesis, Bartın Üniversitesi, Fen Bilimleri Enstitüsü, 2019
  16. Çimento-Genel Çimentolar-Bileşim, Özellikler ve Uygunluk Kriterleri, TS EN 197-1, 2002
  17. Çimento Deney Metot