Failure Analysis of Distributor Gear

İbrahim Yavuz
Pages
63–66
Publication Date
2022-10-19
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

As a result, the occurrence of a ductile fracture was observed and it was determined to be the area where the most critical fracture occurred.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:This study experimentally and theoretically investigated the fracture damage on the distributor gear of a front-wheel drive automobile.
📊
Key Findings & Data:The experimental stud-ies initially analyzed the fracture surfaces of the gear in the scanning electron microscope (SEM).
💡
Conclusion & Impact:As a result, the occurrence of a ductile fracture was observed and it was determined to be the area where the most critical fracture occurred.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Failure Analysis · Distributor Gear · Finite Element Method

Abstract

This study experimentally and theoretically investigated the fracture damage on the distributor gear of a front-wheel drive automobile. The experimental stud-ies initially analyzed the fracture surfaces of the gear in the scanning electron microscope (SEM). Subsequently, microstructure analysis and mechanical tests were performed. In the theoretical study, on the other hand, static analyses were performed using the finite element method on the ANSYS software program. Static analyses revealed equivalent stresses on the piece and determined its criti-cal regions. Finally, the theoretical and experimental studies were compared with literature data. As a result, the occurrence of a ductile fracture was observed and it was determined to be the area where the most critical fracture occurred.

🔖

Cite This Article

Yavuz, İ. (2022). Failure Analysis of Distributor Gear. International Journal of Automotive Science and Technology, Cilt: 5 - Sayı: 1, 63–66. https://ajindex.com/articles/540449

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (13)

  1. Osman A. (2006). Fatigue failure of a helical gear in a gearbox. Eng Fail Anal, 13, 1116–1125
  2. Kovan V., Sekercioglu T. (2007). Pitting failure of truck spiral bevel gear. Eng Fail Anal, 14, 614–619
  3. Park S., Lee L., Moon U., Kim D. (2010). Failure analysis of a planetary gear carrier of 1200HP transmission. Eng Fail Anal, 17, 521–52
  4. Yu Z., Xu X., (2010). Failure investigation of a truck diesel engine gear train consisting of crankshaft and camshaft gears. Eng Fail Anal, 17, 537–545
  5. Rivera R., Chiminelli A., Gómez C., Núñez J.L. (2010). Fatigue failure analysis of a spring for elevator doors. Eng Fail Anal, 17, 731–738
  6. Peng C., Liu, Z., Zhu W. (2011). Failure analysis of a gear tooth facture of a rolling mill decelerator. Eng Fail Anal, 18, 25–35
  7. Heyes A.M. (1998). Automotive component failures. Eng Fail. Anal., 2, 129–141
  8. Bayrakceken H., Tasgetiren S., Yavuz İ. (2007). Two cases of failure in the power transmission system on vehicles: A universal joint yoke and a drive shaft. Eng Fail Anal, 14, 716-724 [9] Yavuz İ., Bayrakçeken H. (2011). Failure Analysis of A Rear Axle Shaft of An Automobile. Electronic Journal of Vehicle Technologies, 3, 11-19 [10] Matveb.com/search/datasheet.aspx?matguid=00c8d94116c a4b32865b7999b0241cc6&n=1&ckck=1-2020 [11] Barker V. M., Johnson W. S., Adair B. S., Antolovich S. D., Staroselsky A. (2013). Load and temperature interaction modeling of fatigue crack growth in a Ni-base superalloy. International Journal of Fatigue, 52, 95–105
  9. Liu H., Bao R., Zhang J., Fei B. (2014). A creep–fatigue crack growth model containing temperature and interactive effects. International Journal of Fatigue, 59, 34–42
  10. Mahobia G.S., Paulose N., Mannan S.L., Sudhakar R.G., Chattopadhyay K., Srinivas N. C. S., Singh V. (2014). Ef-fect of hot corrosion on low cycle fatigue behavior of sup-eralloy IN718. Int. Journal of Fatigue, 59, 272–281
  11. Li Y.D., Liu C.B., Xu N., Wu X.F., Guo W.M., Shi J.B., (2013). A failure study of the railway rail serviced for heavy cargo trains. Case Studies in Engineering Failure Analysis, 1, 243–248
  12. Hormaza W., Mateus L., Maranon A. (2009). Failure anal-ysis of a cylinder sleeve from a turbocharged diesel engine, Engineering Failure Analysis, 16, 1355–1365 [16] Bayrakceken H., Tasgetiren S., Aksoy F. (2007). Failures of single cylinder diesel engines crank shafts, Engineering Failure Analysis, 14, 725–730
  13. Pantazopoulos G., Vazdirvanidis A., Rikos A., Toulfatzis