AI Summary & Key Takeaways
AI InsightIts glass transition temperature has been obtained from inverse gas chromatography data as comparing with that of DSC curve.
📌 3 Key Takeaways
Abstract
Inverse gas chromatographic studies have been carried out on systems consisting of styrene (61%)-ethylmethacrylate (39%) copolymer and ethanol, methanol, propanol, butanol, pentanol, n-hexane, n-pentane, n-octane and n-decane as probes. At infinite dilution Flory-Huggins interaction parameter$(chi)$, weight fraction activity coefficients $(a_1/w_1)^infty$, excess partial molar free energy of mixing $Deltaoverline{G}_1^infty$ have been computed for these systems in the range 403 - 443 K, above glass transition temperature of the copolymer. The solubility parameter $(delta_2)$ of copolymer have been found in the same temperature range and it has been estimated $delta_2$ value at 298 K from data above temperature range. Its glass transition temperature has been obtained from inverse gas chromatography data as comparing with that of DSC curve.
Özet
Çözücü olarak etanol, metanol, propanol, bütanol, pentanol, n-hekzan, n-heptan, n-oktan ve n-dekan gibi çözücüler kullanılarak stiren (61%)-etilmetakrilat (39%) kopolimer sistemi üzerinde invers gaz kromatografik çalışmalar yapılmıştır. Kopolimerin camsı geçiş sıcaklığı üstünde 403-443 K aralığında sonsuz seyreltik hal için probların Flory-Huggins etkileşim parametresi $(chi)$, ağırlıkları aktiflik katsayıları $(a_1/w_1)^infty$, karışımın kısmi molar serbest enerjisi $Deltaoverline{G}_1^infty$ hesaplandı. Kopolimerin çözünürlük parametresi $(delta_2)$ aynı sıcaklık aralığında bulundu ve 298 K'de $delta_2$ hesaplandı. Kopolimerin camsı geçiş sıcaklığı invers gaz kromatografî verilerinden elde edildi ve DSC eğrisiyle karşılaştırmalı olarak verildi.