As a result, it was determined that the added alloying elements increased the mechanical properties, but the mechanical properties decreased with the amount of alloying elements increasing after 1% wt. due to the powder metallurgy process.
📌 3 Key Takeaways
🎯
Objective & Hypothesis:In this study, the effect of Cr-Ni addition on the mechanical properties of plain carbon steel was investigated.
📊
Key Findings & Data:For this purpose, Cr-Ni (wt. % 0.5-3) was added to the matrix containing 0.5 C with powder metallurgy method.
💡
Conclusion & Impact:As a result, it was determined that the added alloying elements increased the mechanical properties, but the mechanical properties decreased with the amount of alloying elements increasing after 1% wt. due to the powder metallurgy process.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Toz metalürjisi · Alaşımlı çelik · Mekanik özellikler
Özet
In this study, the effect of Cr-Ni addition on the mechanical properties of plain carbon steel was investigated. For this purpose, Cr-Ni (wt. % 0.5-3) was added to the matrix containing 0.5 C with powder metallurgy method. The tensile test, micro hardness measurement and microstructure analysis were performed to investigate the effect of the additions on the mechanical properties. As a result, it was determined that the added alloying elements increased the mechanical properties, but the mechanical properties decreased with the amount of alloying elements increasing after 1% wt. due to the powder metallurgy process.
ERDEN, M. A., DEMİRTAŞ, H. (2022). Cr ve Ni İlavesinin Sade Karbonlu Çeliğin Mekanik Özelliklerine Etkisi. Düzce Üniversitesi Bilim ve Teknoloji Dergisi, Cilt: 7 - Sayı: 3, 1217–1223. https://ajindex.com/articles/494377
K. S. Narasimhan, “Sintering of powder mixtures and the growth of ferrous powder metallurgy,” Mater. Chem. Phys., vol. 67, no. 1–3, pp. 56–65, 2001
M. A Erden,, S. Barlak,, B. Adalı,, Ö. Çelikkıran, "Toz Metalurjisi İle Üretilen Nb-V Mikroalaşim Çeliğine Vanadyum İlavesinin Mikroyapi Mekaniksel Özellikleri Üzerine Etkisi". Düzce Üniversitesi Bilim ve Teknoloji Dergisi, vol. 6, pp. 629-636, 2018
H. Danninger and C. Gierl, “New alloying systems for ferrous powder metallurgy precision parts,” Sci. Sinter., vol. 40, no. 1, pp. 33–46, 2008
O. Bergman, “Influence of oxygen partial pressure in sintering atmosphere on properties of Cr–Mo prealloyed powder metallurgy steel,” Powder Metall., vol. 50, no. 3, pp. 243–249, 2007
Tekeli, S., Güral, A. 2007. "Dry sliding wear behaviour of heat treated iron based powder metallurgy steels with 0.3% Graphite + 2% Ni additions". Materials and Design, 28(6), 1923–1927
M. A. Razzak, “Heat treatment and effects of Cr and Ni in low alloy steel,” Bull. Mater. Sci., vol. 34, no. 7, pp. 1439–1445, 2011
M. A. Erden and R. Gunduz, “Effect of Cr Content on Microstructure and Tensile Strength Properties of Cr Added Steel Produced By Powder Metallurgy Method
International Iron & Steel Symposium, pp. 609-611
S. H. Avner, Introduction to physical metallurgy, 2nd ed. McGraw, 1974
M. A. Erden, “Investıgatıon Of The Effect Of Nickel Content On Mıcrostructure And Mechanıcal Propertıes Of Non Alloyed Steels Producted By Powder Metallurgy”, GU J Sci Part:C, vol. 4 no. 4, pp. 241-245, 2016
U. Lindstedt, B. Karlsson, and R. Masini, “Influence of porosity on deformation and fatigue behavior of P/M austenitic stainless steel,” Int. J. Powder Metall. (Princeton, New Jersey), vol. 33, pp. 49–61, 1997
H. Danninger, R. Pöttschacher, S. Bradac, A. Šalak, and J. Seyrkammer, “Comparison of Mn, Cr and Mo alloyed sintered steels prepared from elemental powders,” Powder Metall., vol. 48, no. 1, pp. 23–32, 2005
A. Molinari, G. Straffelini, and P. Campestrini, “Influence of microstructure on impact and wear behaviour of sintered Cr and Mo steel,” Powder Metall., vol. 42, no. 3, pp. 235–241, 1999
D. Shanmugasundaram and R. Chandramouli, “Tensile and impact behaviour of sinter-forged Cr, Ni and Mo alloyed powder metallurgy steels,” Mater. Des., vol. 30, no. 9, pp. 3444–3449, 2009.