AI Summary & Key Takeaways
AI InsightThis agglomeration deteriorated the mechanical properties of nano alumina reinforced aluminum composites.
📌 3 Key Takeaways
Abstract
In the present work, nano alumina (Al2O3) reinforced aluminum (Al) matrix composites with various alumina content (0-2.5wt.%) were fabricated by powder metallurgy method. This method occurs of mixing, ultrasonic dispersion, filtering, drying, pressing, and sintering processes. The effects of nano alumina amount on the Vickers hardness, apparent density, compressive strength, and microstructure of nano alumina reinforced aluminum matrix composites were investigated. The maximum apparent density (2.66 g/cm3), Vickers hardness (43±1 HV), and compressive strength (130±3 MPa) were determined at Al-2wt.%Al2O3 composite. After 2wt.% nano alumina content, the agglomeration was detected by a scanning electron microscope (SEM). This agglomeration deteriorated the mechanical properties of nano alumina reinforced aluminum composites.
Özet
Bu çalışmada nano alümina (Al2O3) takviyeli alüminyum (Al) matrisli kompozitler (ağ. % 0-2.5) toz metalurjisi yöntemiyle üretilmiştir. Bu yöntem karıştırma, ultrasonik dağıtma, filtreleme, kurutma, presleme ve sinterleme işlemlerinden oluşmaktadır. Nano alümina miktarının Vickers sertliği, yoğunluk, basma dayanımı ve kompozitlerin mikroyapıları üzerindeki etkileri incelenmiştir. Maksimum yoğunluk (2.66 g/cm3), Vickers sertliği (43±1 HV) ve basma dayanımı (130±3 MPa), ağırlıkça % 2 Al2O3 takviyeli Al kompozit yapıda elde edilmiştir. Ağırlıkça %2 nano alümina katkısından sonra, topaklanma oluşumu taramalı elektron mikroskobu (SEM) ile tespit edilmiştir. Bu topaklanmalar nano alümina takviyeli alüminyum kompozitlerin mekanik özelliklerini olumsuz etkilemiştir.