AI InsightTexture analysis of a Cu-10 % Ni alloy carried out on three types of cast materials after varying amounts of deformation led to clearly defined copper type texture due to the dominance of high stacking fault energy SFE regions in the structure. (123) [41 2 ] is the strongest orientation observed with (123) as the plane lying paralel to the rolling plane and [41 2 ] as the direction paralel to the rolling direction.
📌 3 Key Takeaways
Abstract
Non-random distribution of orientations between the neigbouring grains of polycrystalline aggregates leads to preferred orientations or textures. Texture analysis of a Cu-10 % Ni alloy carried out on three types of cast materials after varying amounts of deformation led to clearly defined copper type texture due to the dominance of high stacking fault energy SFE regions in the structure. (123) [41 2 ] is the strongest orientation observed with (123) as the plane lying paralel to the rolling plane and [41 2 ] as the direction paralel to the rolling direction.
Özet
Polikristalin malzemelerde komşu taneler arasındaki yerleşim ilişkileri tercihli yerleşim veya örgüyü ortaya çıkarır. Üç farklı tip döküm prosesi ve farklı deformasyon seviyeleri sonrası Cu-% 10 Ni alaşımlarından alınan numuneler üzerinde yapılan analiz, yapıda hakim durumda olan yüksek istif hatası enerjisinden dolayı bakır tipi örgüyü açık bir şekilde ortaya çıkarmıştır. Gözlenen en kuvvetli yerleşim, haddeleme düzlemine paralel (123) düzlemi ve haddeleme yönüne paralel [41 2 ] yönünden oluşan (123) [41 2 ] olmuştur.