Thesamples prepared through this process were subjected to tension test according to DIN 53255 standarts.Based on initial results, the best glued resistance was obtained with the samples glued with UF glue (8,59N/mm²), the worst resistance was obtained with the samples attached with PU + %5 Boraks (2,50 N/mm²).
📌 3 Key Takeaways
🎯
Objective & Hypothesis:In this study, the effects of polivinalacetat (PVAc), ure-formaldehyd (UF), polyuretan (PU) glues and theirmodification with borax on bonding resistance of chestnut (Castenea sativa Mill.) wood in the Agean Regionwere evaluated.
📊
Key Findings & Data:For this purpose, the samples prepared from chestnut (Castenea sativa Mill.) woods obtainedfrom Simav in Agean Region were glued with Polivinalacetat (PVAc), Ure-formaldehyd (UF), Polyuretan (PU)glues and with modifications of these glues, PVAc + %5 Boraks, UF + %5 Boraks, PU + %5 Boraks.
💡
Conclusion & Impact:Thesamples prepared through this process were subjected to tension test according to DIN 53255 standarts.Based on initial results, the best glued resistance was obtained with the samples glued with UF glue (8,59N/mm²), the worst resistance was obtained with the samples attached with PU + %5 Boraks (2,50 N/mm²).
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Boraks · Kestane ağacı · Tutkal
Abstract
In this study, the effects of polivinalacetat (PVAc), ure-formaldehyd (UF), polyuretan (PU) glues and theirmodification with borax on bonding resistance of chestnut (Castenea sativa Mill.) wood in the Agean Regionwere evaluated. For this purpose, the samples prepared from chestnut (Castenea sativa Mill.) woods obtainedfrom Simav in Agean Region were glued with Polivinalacetat (PVAc), Ure-formaldehyd (UF), Polyuretan (PU)glues and with modifications of these glues, PVAc + %5 Boraks, UF + %5 Boraks, PU + %5 Boraks. Thesamples prepared through this process were subjected to tension test according to DIN 53255 standarts.Based on initial results, the best glued resistance was obtained with the samples glued with UF glue (8,59N/mm²), the worst resistance was obtained with the samples attached with PU + %5 Boraks (2,50 N/mm²).
Özet
Bu çalışmada, polivinilasetat (PVAc), üre-formaldehit (UF), poliüretan (PU), tutkallarının ve bu tutkalların
ALTINOK, M., ÖZALP, M., KARAASLAN, A., PERÇİN, O. (2009). Effects of Glues Modified with Borax on the Bonding Strength Of Chestnut Wood. Bartın Orman Fakültesi Dergisi, Cilt: 11 - Sayı: 15, 17–24. https://ajindex.com/articles/32374
o Altınok, M.1998. Ağaç İşleri Temel Makinelerinde İşlenmiş Ahşap Yüzeylerin Yapışma Direncine Etkileri, G.Ü.T.E.F. Politeknik Dergisi, Cilt 1, S. 1-2 o Altınok, M., Döngel, N., Söğütlü, C. 1999. Üre formaldehit ile modifiye edilmiş ST10 tutkalının yapışma direncinin belirlenmesi, Teknoloji Dergisi, Z.K.Ü., Karabük Teknik Eğitim Fakültesi, Sayı 3-4, S. 193-201,
Zonguldak. o Altınok, M., Döngel, N., Söğütlü, C., 2000. Modifiye edilmiş polivinilasetat dispersiyonu (VB20) tutkalının yapışma direncinin belirlenmesi, G.Ü., Fen Bilimleri Enstitüsü Dergisi, cilt 13, no:2, Ankara. o Altınok, M., Döngel, N.2002. Çam Türü Lamine Elemanlarda Mekanik Performans, Gazi Üni. - Fen Bil. Enst. Dergisi, cilt:15, No:1, sayfa: 215-225,
Ankara. o Bozkır, S. M., Çeviri 1995. Bor Ekonomisi’’, Raskill Information Services LTD. 2 Clampham Road Londan SW9 Oja – England, S. 145. o Bridaux,V., Charrier,B., Fauroux, N.,Charrier,F., and Goncalez J.2001. Addition of Boron Based Compound in the LVL Glueline, Effect on the Mechanical Properties and the Leaching of Boron, Vol:55. o Chung, Y. 1968. Gulueabilty of Southern Pine Early Wood and Late Wood. F. P. J. 18 (2). 32 – 36. o Demetçi, E.Y. 1991. Önemli Bazı Ağaç Türlerinin PVAc ve Epoksi Tutkalları ile Yapışma Özellikleri Üzerine Araştırmalar. I.Ü. Fen Bilimleri Enstitüsü, Doktora Tezi, İstanbul. o DIN 53255. 1964. Testing of wood adhesives and glued wood joints; shear and delamination tests for determining the failing strength of plywood bonds (plywood and coreboard), Deutsches Institut Fur Normung E.V. (German National Standard) o Efe,H., Gürleyen, L., Kasal, A. 2002. Dört Kesicili Jilet Bıçak Topu İle İşlenmiş Masif Ağaç Malzemede Devir Sayısının Yapışma Performansına Etkileri, GÜ, Fen Bilimleri Dergisi, Nisan 2002 Cilt: 15 No:2, ISSN 1300-1833 o Kocatürk, İ. 2000. Sentetik Tutkallarda Modifikasyonun Ağaç Malzemede Yapışma Direncine Etkileri, Yüksek Lisans Tezi Gazi Üniversitesi Fen Bilimleri Enstitüsü, S. 43 (yayımlanmamış) o Örs, Y., Altınok, M., Kocatürk, İ., Modification In The Wood Adhesives And Determination of Bonding Performances, Journal Of Holz Als Roh-Und Werkstoff, München, (hakem görüşünde) o Özcan, M. 1997. Batı Karadeniz Bölgesi İçin Kestane Hacim Tablosunun Düzenlenmesi, Yüksek Lisans Tezi, K.T.Ü. Fen Bilimleri Enstitüsü, 43 s. (yayımlanmamış) o Şenay, A. 1996. ''Ahşap Lamine Taşıyıcı Elemanların Mekanik Özelliklerinin Belirlenmesi Üzerine Araştırmalar'', İÜ,F.B.E., Doktora Tezi, İstanbul. o TS 53. Odunun Fiziksel Öze