AI InsightAs a result, increasing the rate of sepiolite in aerated concrete decreases the compressive strength and increases the thermal conductivity.
📌 3 Key Takeaways
Abstract
Aerated concrete is a lightweight concrete which has porous structure. In this study, effects of usage of sepioliteas a raw material instead of quartzite on the thermal and compressive strength properties of aerated concrete were investigated.G2/04 class aerated concrete, which has been commercially produced as a wall component, has been focused. Aerated concrete samples have been prepared by substitution of sepiolite instead of quartzite in %5, %10, %15, %20 and %25. Sepiolite has been provided from Eskişehir mine field. After 4 hours cure at 60ºC, samples moved to treat in autoklave in the temperature of 180ºC and pressure at 11 bar for 6.5 hours. Thermal conductivity and compressive strength properties of samples were determined. As a result, increasing the rate of sepiolite in aerated concrete decreases the compressive strength and increases the thermal conductivity.
Özet
Gazbeton gözenekli hafif betondur. Bu araştırmada, Sepiyolitin gazbeton üretiminde hammadde olarak kullanılan kuvarsit yerine ikamesinin gazbetonun ısıl ve basınç dayanım özelliklerine etkisi araştırılmıştır. Araştırmada, duvar elamanı olarak kullanılan ve ticari olarak üretimi yapılan G2/04 sınıfı gazbeton üretimi esas alınmıştır. Eskişehir Sivrihisar maden sahasından alınan Sepiyolitin, hammadde olarak kullanılan kuvarsit yerine %5, %10, %15, %20 ve %25 oranlarında ikame edilerek gazbeton örnekleri üretilmiştir. Üretilen örnekler 60 ºC sıcaklıkta 4 saat kürde bekletildikten sonra 180 ºC'de 11 bar basınçta 6,5 saat otoklavda küre tabi tutulmuştur. Üretilen örneklerin basınç dayanımı ve ısıl iletkenlik özellikleri belirlenmiştir. Sonuç olarak sepiyolit oranının arttırılması sonucu basınç dayanımında azalma olurken ısıl iletimde iyileşme gözlenmiştir.