AI InsightHigher surface roughness of the PM parts, increased the coating surface area and more coating materials were used compared to rolled samples.
📌 3 Key Takeaways
Abstract
In this study, the coatability of powder metallurgy parts by PVD (Physical Vapour Deposition) technique was investigated. Commençai Fe and Cu powders were compacted at different pressures and sintered to obtain PM (Powder Metal) Parts. PM parts and rolled Cu, and transmission steel were coated by TiN with PVD and the coatability of the parts was compared with the above materials. Coating interfaces were investigated by scanning electron microscopes. Coating thickness depending on coating conditions and type of materials were determined. Higher surface roughness of the PM parts, increased the coating surface area and more coating materials were used compared to rolled samples.
Özet
Bu çalışmada; toz metalürjisi yöntemi ile üretilmiş parçaların PVD (Fiziksel Buhar Çöktürme) yöntemi ile kaplanabilirliği araştırıldı. Toz metal parçalar ticari saflıkta Fe ve Cu tozlarından değişik basınçlarda preslenip sinterlenerek elde edildi. Bu malzemelerin kaplanabilirliğini hadde ürünü Cu ve transmisyon çeliği ile mukayese edebilmek amacıyla aynı boyutlardaki hadde ve transmisyon çeliği aynı şartlarda PVD yöntemi ile TiN kaplandı. Kaplama ara yüzeyi elektron mikroskobunda incelendi. Kaplama şartlarına ve malzeme türüne göre kaplama kalınlığı ölçüldü. Kaplama ağırlığının toz metal parçalarda yüzey pürüzlülüğüne bağlı olarak artan yüzey alanından dolayı daha fazla olduğu görüldü.