The anisotropic behaviour of the mechanical properties of hot rolled round product produced in electric arc furnace was investigated. Tensile and izod impact tests were conducted on the specimens had been cut out in $\phi=0^\circ$, $\phi=45^\circ$° and $\phi=90^\circ$, to the rolling direction. Ductility, tensile stress, yield stress and impact values of these specimens in various directions were examined. Morphologies of fracture surfaces and types of inclusions were investigated by scanning electron microscopy and EDAX analyses respectively. The decrasing on ductility and impact value at the transverse direction were due to the sulphide inclusions which are aligned in the rolling direction of the steel bar were determined. But, yield stress and tensile stress of steel bar were found to be isotropic.
Özet
Elektrik ark ocağında üretilmiş ve sıcak haddelenmiş SAE 8620 yuvarlak çelik çubuğun mekanik özelliklerindeki anizotropik durum incelenmiştir. Haddeleme doğrultusuna $\phi=0^\circ$, $\phi=45^\circ$° ve $\phi=90^\circ$, açı ile hazırlanan çekme ve çentik darbe numunelerine çekme ve izod darbe deneyleri yapılmıştır. Farklı doğrultulardaki bu numunelerin süneklikleri, çekme, akma ve darbe dayanımları belirlenmiştir. Tarama elektron mikroskop çalışmaları ve EDAX analizleri ile kırık yüzey morfolojileri incelenmiş ve inklüzyon türleri belirlenmiştir. Haddeleme doğrultusunda uzamış MnS inklüzyonları sebebi ile çelik çubuğun bu doğrultuya dik doğrultudaki süneklik ve darbe dayanımında aşırı düşüş belirlenmiştir. Ancak, akma ve çekme dayanımında yöne bağlı belirgin bir değişiklik olmamıştır.