AI InsightIt was found that high preheating temperature resulted in an increase in tensile strength and toughness whereas lowered the hardness values.
📌 3 Key Takeaways
Abstract
The aim of this reseach was to find out the effect of preheat treatment on the weldabilites of C 1070 and C 1080 steels. They were welded at room temperature, with preheating temperatures of 250 $\circ_C$ and 350 $\circ_C$ by using basic covered electrodes. Macro and microstructural evaluation, together with tensile, impact and hardness tests were conducted on welded materials. It was found that high preheating temperature resulted in an increase in tensile strength and toughness whereas lowered the hardness values. Furthermore, high preheating temperature resulted in an enlargment of the HAZ and also facilitated the formation of dendritic microstructure in weld bead. These results indicated that these steels could be welded safely with proper preheating treatment.
Özet
Bu çalışmada; karbon eşdeğerliği yüksek olan C 1070 ve C 1080 çeliklerin oda sıcaklığında, 250 $\circ_C$ ve 350 $\circ_C$ ön tav sıcaklığında bazik karakterli örtülü elektrotlarla kaynak edilebilirlikleri araştırılmıştır. Kaynak yapılmış numunelere makro ve mikro yapı incelemesi ile çekme, darbe ve sertlik gibi mekanik testler uygulanmıştır. Mekanik test sonuçları artan ön tav sıcaklığı ile çekme ve çentik mukavemetlerinde artış olduğunu, sertlikte ise düşme olduğunu göstermiştir. Ön tav sıcaklığı arttıkça ITAB'ın genişlediği ve kaynak metalinin dentiritik olarak katılaştığı görülmüştür. Bu çalışma ile kaynak öncesi ve kaynak sonrası özel önlemler alındığında karbon eşdeğerliği yüksek çeliklerin kaynak edilebildikleri görülmüştür.