Abstract
In this study, the effect of casting delay and remixing to the mechanical properties of concrete is put-out. For this purpose concrete mortar was prepared by Çayırhan fly ash which is artificial pozzolan that replacing with 15% cement mass. Fresh concrete was delayed 30, 45, 60, 75 and 90 minutes in five different times. At the end of these times fresh concrete was remixed and obtained 15 cm and 10 cm cube with 10x10x50 cm beam specimens 28 days specimens is used for pressure strenght and yield stress ,60 days specimens is used for abrasion strenght
Özet
Bu çalışmada, betonun mekanik özellikleri üzerine bekleme süresi ve tekrar karıştırma işleminin etkisi araştırılmıştır. Bu amaçla yapay bir puzolan olan Çayırhan uçucu külü çimentonun ağırlıkça % 15’i yerine ikame edilerek beton harcı hazırlanmıştır. Taze beton 30, 45, 60, 75 ve 90 dakika olmak üzere 5 farklı sürede bekletilmiştir. Bu sürelerin sonunda taze beton tekrar karıştırılarak 10 cm ve 15 cm’lik küp ile 10x10x50 cm’lik kiriş numuneler elde edilmiştir. Basınç ve eğilme dayanımları 28 gün, aşınma dayanımı ise 60 günlük numuneler kullanılarak belirlenmiştir. Sonuç olarak en yüksek dayanımlar, 30 dakika bekletilen betondan elde edilmiştir.