AI InsightExperimental results showed that, pulsed current leads to low heat input, grain refinement and hardness increase in weld metal compared to alternative current were used.
📌 3 Key Takeaways
Abstract
In this study, AA 4000 series Al-Si alloys sheets were joined by TIG welding method using alternative and pulsed current. Tensile test, bending test, hardness test and microstructure examination of joined test specimens were carried out in order to see the effect of current type on mechanical properties of welded samples. Experimental results showed that, pulsed current leads to low heat input, grain refinement and hardness increase in weld metal compared to alternative current were used. Specimens joined by the pulsed current showed higher tensile strength than the specimens welded by the alternative current. After bending test, cracks, tearing and surface defection were not observed on the samples
Özet
Bu çalışmada, AA 4000 serisi Al-Si alaşımı levhalar TIG kaynak yöntemi ile alternatif ve darbeli akım kullanılarak birleştirilmişlerdir. Kullanılan akım türünün kaynaklı birleştirmenin özelliklerine olan etkilerini görmek amacı ile birleştirilen numunelere mikroyapı, çekme, sertlik ve eğme testleri uygulanmıştır. Deneyler sonucunda, darbeli akımın düşük ısı girdisine, kaynak metalinde tane incelmesine ve alternatif akıma göre kaynak metali sertliğinde artışa neden olduğu belirlenmiştir. Birleştirmelere uygulanan çekme testlerinde, darbeli akım ile birleştirilen numunelerin alternatif akıma nazaran daha yüksek çekme dayanımı gösterdikleri tespit edilmiştir. Yapılan eğme testi sonucunda numunelerde yırtılma ve çatlak oluşumu gibi bir yüzey hatasına rastlanılmamıştır.