Wood Property Improvement of Siberian Pine by Combination of Boric Acid Impregnation and In-Situ Polymerization of Ԑ-Caprolactone

Mahmut Ali ERMEYDAN
Eylem DİZMAN TOMAK
Zeynep Nur KARTAL
Pages
157–161
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

The results showed that leached samples had lower weight loss than unleached samples after C. puteana attack, however, the weight loss by C. versicolor attack increased in leached samples.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:Wood is an excellent engineering material with its light weight and high mechanical properties.
📊
Key Findings & Data:In the study, Siberian pine samples were impregnated with 1% boric acid in DMF(N,N-Dimethylformamide) and further ε-caprolactone monomer (1% SnOct2 as initiator) mixture for further in-situ polymerization were carried out in the oven at 150°C for 3 hours.
💡
Conclusion & Impact:The results showed that leached samples had lower weight loss than unleached samples after C. puteana attack, however, the weight loss by C. versicolor attack increased in leached samples.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Poly(ε-caprolactone) · wood modification · dimensional stability

Abstract

Wood is an excellent engineering material with its light weight and high mechanical properties. However, it is susceptible to biodegradation due to its hygroscopic nature and chemical composition that limits both its indoor and outdoor usage. Boron compounds which are known as eco-friendly wood preservatives have limited utility at outdoor conditions since they are easily leached out from wood by water. The aim of this study is to prevent boron leaching by creating a polymer network that encapsulates boron compound inside the wood cell walls, thus decay resistance, dimensional stability and water repellence are improved. In the study, Siberian pine samples were impregnated with 1% boric acid in DMF(N,N-Dimethylformamide) and further ε-caprolactone monomer (1% SnOct2 as initiator) mixture for further in-situ polymerization were carried out in the oven at 150°C for 3 hours. Prior to decay testing, leaching test was conducted in order to evaluate any loss in effectiveness in decay resistance against to C. puteana and C. versicolor attack due to possibility of boron leaching from wood. The results showed that leached samples had lower weight loss than unleached samples after C. puteana attack, however, the weight loss by C. versicolor attack increased in leached samples. Decay resistance of treated samples was found to be 7-99% in comparison with references. Boric acid and polymer combination increased dimensional stability (25% ASE), and water repellence (15%) of wood compared to references without deformation. This method showed that curing may be an alternative for wood modification with in-situ polycaprolactone polymerization in order to use hazardous solvent media for polymerization.

Özet

Wood is an excellent engineering material with its light weight and high mechanical properties. However, it is susceptible to biodegradation due to its hygroscopic nature and chemical composition that limits both its indoor and outdoor usage. Boron compounds which are known as eco-friendly wood preservatives have limited utility at outdoor conditions since they are easily leached out from wood by water. The aim of this study is to prevent boron leaching by creating a polymer network that encapsulates boron compound inside the wood cell walls, thus decay resistance, dimensional stability and water repellence are improved. In the study, Siberian pine samples were impregnated with 1% boric acid in DMF(N,N-Dimethylformamide) and further ε-caprolactone monomer (1% SnOct2 as initiator) mixture for further in-situ polymerization were carried out in the oven at 150°C for 3 hours. Prior to decay testing, leaching test was conducted in order to evaluate any loss in effectiveness in decay resistance against to C. puteana and C. versicolor attack due to possibility of boron leaching from wood. The results showed that leached samples had lower weight loss than unleached samples after C. puteana attack, however, the weight loss by C. versicolor attack increased in leached samples. Decay resistance of treated samples was found to be 7-99% in comparison with references. Boric acid and polymer combination increased dimensional stability (25% ASE), and water repellence (15%) of wood compared to references without deformation. This method showed that curing may be an alternative for wood modification with in-situ polycaprolactone polymerization in order to use hazardous solvent media for polymerization.

🔖

Cite This Article

ERMEYDAN, M. A., TOMAK, E. D., KARTAL, Z. N. (2019). Wood Property Improvement of Siberian Pine by Combination of Boric Acid Impregnation and In-Situ Polymerization of Ԑ-Caprolactone. Politeknik Dergisi, Cilt: 22 - Sayı: 1, 157–161. https://ajindex.com/articles/306441

References (2)

  1. 1] Hill C. A. S., “Wood modification: chemical, thermal and other processes”, John Wiley & Sons, Chichester, England, Hoboken, NJ, (2006). [2] Rowell R. M., “Handbook of Wood Chemistry and Wood Composites”, CRC Press,
  2. Boca Raton, FL, (2000). [3] Kartal S. N., Yoshimura T., Imamura Y., “Decay and termite resistance of boron-treated and chemically modified wood by in situ co-polymerization of allyl glycidyl ether (AGE) with methyl methacrylate (MMA)”, International Biodeterioration & Biodegradation, 53(2): 111-117, (2004). [4] Yalinkilic M. K., Gezer E. D., Tkahashi M., Demirci Z., Ilhan R., Imamura Y., “Boron addition to non or low-formaldeyde cross-linking reagents to enhance biological resistance and dimensional stability of wood”, Holz als Roh- und Werkstoff, 57: 351-357, (1999). [5] Dauvergne E. T., Soulounganga P., Gerardin P., Loubinoux B., “Glycerol/glyoxal: a new boron fixation system for wood preservation and dimensional stabilization”, Holzforschung, 54: 123–126, (2000). [6] Temiz A., Alfredsen G., Eikenes M., Terziev N., "Decay Resistance Of Wood Treated With Boric Acid And Tall Oil Derivates", Bioresource Technology, 99: 2102-2106, (2008). [7] Kartal S. N., Yoshimura T., Imamura Y., “Modification of wood with Si compounds to limit boron leaching from treated wood and to increase termite and decay resistance”, International Biodeterioration & Biodegradation, 63:187–190, (2009). [8] Jebrane M. and Heinmaa I., “Covalent fixation of boron in wood through transesterification with vinyl ester of carboxyphenylboronic acid”, Holzforschung, 70(6): 577-583, (2015). [9] Ermeydan M. A., Cabane E., Hass P., Koetz J., Burgert I., “Fully biodegradable modification of wood for improvement of dimensional stability and water absorption properties by poly(ε-caprolactone) grafting into the cell walls”, Green Chemistry, 16(6): 3313-3321, (2014). [10] Rowell R. M. and Ellis W. D., “Determination of dimensional stability of wood using the water-soaking method”, Wood and Fiber, 10(2): 104-111, (1978). [11] Zabel R. A., Morrell J. J., “Wood Microbiology Decay and Its Prevention”, Academic Press: San Diego, (1992). [12] Mantanis G. I., Young R. A., and Rowell R. M., “Swelling of wood, part II. Swelling in organic liquids”, Holzforschung, 48: 480-490, (1994). [13] Ermeydan M. A., Tomak E. D., “The Combined Effects of Boron and Polymer Modification on Decay Resistance and Properties of Wood”, 16th International Materials Symposium, Denizli, 1574-1581, (2016). [14] Reinpre