Farklı yöntemlerle polimerize edilen kopolimer akrilik rezinlerin mekanik özelliklerinin ve artık monomer içeriğinin değerlendirilmesi

Evaluation of the mechanical properties and residual monomer content of copolymer acrylic resins polymerized by different methods

Ayşegül KÖROĞLU
ONUR ŞAHİN
Doğu Ömür DEDE
Şeyda ADIGÜZEL
Baki HAZER
Pages
31–38
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

Bununla birlikte işlem, bazı rezin gruplarının artık monomer miktarında artışa neden olmuştur.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:Amaç: Bu çalışmanın amacı dört farklı monomer eklenerek kopolimerizasyon mekanizmasıyla polimerize olmuş protez kaide rezinlerinin bükülme dayanımı, elastik modulus, çarpma dayanımı ve artık monomer içeriğinin değerlendirilmesidir.
📊
Key Findings & Data:Gereç ve Yöntemler: Bütil metakrilat (BMA), isobütil metakrilat (IBMA), 2-hidroksietil metakrilat (HEMA) ve metakril-polihedral silseskioksan (POSS-MA) hacimce %2, %5 ve %10 konsantrasyonlarında konvansiyonel ısı (HP) ve mikrodalga (MP) akrilik monomerlerine ilave edilmiştir.
💡
Conclusion & Impact:Bununla birlikte işlem, bazı rezin gruplarının artık monomer miktarında artışa neden olmuştur.
🔬Design:Research Article
📍Scope:Comprehensive Sample
⚙️Variables:Domain Parameters

Abstract

Amaç: Bu çalışmanın amacı dört farklı monomer eklenerek kopolimerizasyon mekanizmasıyla polimerize olmuş protez kaide rezinlerinin bükülme dayanımı, elastik modulus, çarpma dayanımı ve artık monomer içeriğinin değerlendirilmesidir. Gereç ve Yöntemler: Bütil metakrilat (BMA), isobütil metakrilat (IBMA), 2-hidroksietil metakrilat (HEMA) ve metakril-polihedral silseskioksan (POSS-MA) hacimce %2, %5 ve %10 konsantrasyonlarında konvansiyonel ısı (HP) ve mikrodalga (MP) akrilik monomerlerine ilave edilmiştir. Universal test cihazı ve Charpy tip çarpma test cihazı ile örneklerin bükülme dayanımı, elastik modulusu ve çarpma dayanımı ölçülmüştür. Yüksek performanslı sıvı kromatografisi (HPLC) metoduyla artık monomer içerikleri belirlenmiştir. Bulgular: %10 IBMA ve %10 HEMA, HP rezinlerin bükülme dayanımını artırmıştır. MP rezin grubunun elastik modulusu için kontrol grubu ile %2 ve %5 IBMA, %5 ve %10 HEMA ve %5 POSS-MA grupları arasında anlamlı farklılıklar gözlenmiştir (P<0.05). Kopolimerizasyon mekanizmasının protez kaide rezinlerinin çarpma dayanımı üzerinde olumlu bir etkisi olmamıştır. HP rezin kontrol grubu ile % 10 IBMA, % 10 BMA, %10 POSS-MA grupları arasında artık monomer bakımından anlamlı farklılıklar saptanmıştır (P<0.05). MP rezinde ise kontrol grubu ile %5 IBMA ve %2-5-10 HEMA grupları arasında anlamlı farklılıklar gözlenmiştir (P<0.05). Sonuç: Kopolimerizasyon işlemi %10 IBMA ve %10 HEMA eklenmiş HP protez kaide rezinlerinin bükülme dayanımında etkili olmuştur. Bununla birlikte işlem, bazı rezin gruplarının artık monomer miktarında artışa neden olmuştur.

Özet

Background: The aim of this study was to evaluate the effect of adding four different monomers on the flexural strength, elastic modulus, impact strength and residual monomer content of denture base resins polymerized by copolymerization mechanism. Methods: Butyl methacrylate (BMA), Isobutyl mathacrylate (IBMA), 2-hydroxyethyl methacrylate (HEMA) and methacryl-polyhedral silses quioxane (POSS-MA) were added to monomers of conventional heat (HP) and microwave polymerized (MP) polymethyl methacrylate (PMMA) resin at the concentrations of 2%, 5% and 10% per volume. The flexural strength, elastic modulus and impact strength of specimens were measured with an universal testing machine and Charpy-type impact tester. Residual monomer contents were determined by high performance liquid chromatography (HPLC) method. Results: 10% IBMA and 10% HEMA enhanced the flexural strength of HP resin. For the elastic modulus of MP resin, significant differences observed between the control group and 2 and 5% IBMA, 5 and 10% HEMA, and 5% POSS-MA groups (P<0.05). Copolymerization mechanism had no positive effect on the impact strength of denture base resins. Significant differences were observed between the residual monomer of control group and 10% IBMA, 10% BMA, 10% POSS-MA groups of HP resin (P<0.05). In MP resin group significant differences were observed between control group and 5% IBMA, 2-5-10% HEMA groups (P<0.05). Conclusion: Copolymerization process was effective on the flexural strength of HP denture base resin with 10% IBMA and 10 % HEMA. However the process caused an increase in the residual monomer content of some resin groups.

🔖

Cite This Article

KÖROĞLU, A., ŞAHİN, O., DEDE, D. Ö., ADIGÜZEL, Ş., HAZER, B. (2018). Farklı yöntemlerle polimerize edilen kopolimer akrilik rezinlerin mekanik özelliklerinin ve artık monomer içeriğinin değerlendirilmesi. Selcuk Dental Journal, Cilt: 5 - Sayı: 1, 31–38. https://ajindex.com/articles/301741

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (13)

  1. Jagger DC, Harrison A, Jandt KD. The reinforcement of dentures. J Oral Rehabil 1999; 26(3): 185-94. Nishii M. Curing of denture base resins with microwave irradiation: with particular reference to heat-curing resins. J Osaka Dent Univ 1968; 2(1): 23-40.
  2. Ayaz EA, Durkan R, Bagis B. The effect of acrylamide incorporation on the thermal and physical properties of denture resins. J Adv Prosthodont 2013; 5(2): 110-7.
  3. Polyzois G, Andreopoulos AG, Lagauvardos PE. Acrylic resin denture repair with adhesive resin and metal wires: effects on strength parameters. J Prosthet Dent 1996; 75(4): 381-7.
  4. Köroğlu A, Özdemir T, Usanmaz A. Comparative study of the mechanical properties of fiber-reinforced denture base resin. J App Polymer Sci 2009; 113(2): 716-20.
  5. Sahin O, Ozdemir AK, Turgut M, Boztug A, Sumer Z. Investigation of flexural strength and cytotoxicity of acrylic resin copolymers by using different polymerization methods. J Adv Prosthodont 2015; 7(2): 98-107. Rodford RA. Further development and evaluation of high impact strength denture base materials. J Dent 1990; 18(3): 151-7.
  6. Cunha TM, Regis RR, Bonatti MR, de Souza RF. Influence of incorporation of fluoroalkyl methacrylates on roughness and flexural strength of a denture base acrylic resin. J Appl Oral Sci 2009; 17(2): 103-7.
  7. Hogt AH, Dankert J, Feijen J. Adhesion of coagulasenegative staphylococci to methacrylate polymers and copolymers. J Biomed Mater Res 1986; 20(4): 533-45.
  8. Hamza TA, Johnston WM, Schricker SR. Effect of polyhedral silsesquioxane (POSS) on the flexural strength and color of interim materials. J Prosthet Dent 2014; 112(2): 228-34.
  9. Vallittu PK, Ruyter IE, Buykuilmaz S. Effect of polymerization temperature and time on the residual monomer content of denture base polymers. Eur J Oral Sci 1998; 106(1): 588-93.
  10. Doğan A, Bek B, Çevik NN, Usanmaz A. The effect of preparation conditions of acrylic denture base materials on the level of residual monomer, mechanical properties and water absorption. J Dent 1995; 23(5): 313-8.
  11. Bartoloni JA, Murchison DF, Wofford DT, Sarkar NK. Degree of conversion in denture base materials for varied polymerization techniques. J Oral Rehabil 2000; 27(6): 488-93.
  12. Mohamed SH, Al-Jadi AM, Ajaal T. Using of HPLC analysis for evaluation of residual monomer content in denture base materials and their effect on mechanical properties. J Phy Sci 2008; 19(2): 127-35.
  13. Tsuchiya H, Hoshino Y, Kato H, Takagi N. Flow injection analysis of formaldehyde leached from denture-base acrylic