The Comparison of the Properties of Geopolymer Paste and Ordinary Portland Cement Mortar Produced Using Polycarboxylate Based Admixture

Evren Arıöz(Eskişehir Teknik Üniversitesi)0000-0003-4862-5467
Gamze Saraç(ESKISEHIR TECHNICAL UNIVERSİTY, FACULTY OF ENGINEERING)0000-0003-0407-5192
Ömer Arıöz(TOROS ÜNİVERSİTESİ, REKTÖRLÜK)0000-0002-4070-514X
Ö. Mete Koçkar(ESKISEHIR TECHNICAL UNIVERSİTY, FACULTY OF ENGINEERING)0000-0002-8860-9309
Pages
537–540
Publication Date
2022-03-31
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

The highest compressive strength was obtained as 38.3 MPa for mortar sample aged for 28 days and was 15.3 MPa for geopolymer samples.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:Chemical admixtures are generally used in ready mixed concrete production to improve and enhance the concrete properties.
📊
Key Findings & Data:Polycarboxylate based superplasticizers are classified as third generation plasticizing admixtures which increase fluidity and workability without decreasing compressive strength.
💡
Conclusion & Impact:The highest compressive strength was obtained as 38.3 MPa for mortar sample aged for 28 days and was 15.3 MPa for geopolymer samples.
🔬Design:Araştırma Makalesi
📍Scope:Comprehensive Sample
⚙️Variables:Plasticizer · Cement mortar · Geopolymer

Abstract

Chemical admixtures are generally used in ready mixed concrete production to improve and enhance the concrete properties. Polycarboxylate based superplasticizers are classified as third generation plasticizing admixtures which increase fluidity and workability without decreasing compressive strength. Geopolymers having many superior properties are alternative materials to ordinary Portland cement concrete. Geopolymers are environmentally friendly and sustainable materials because they can be synthesized from waste materials such as fly ash. In this experimental study, geopolymer pastes were produced by using fly ash, 10 M sodium hydroxide, sodium silicate solution and plasticizer. Cement mortars were produced according to TS EN 196-1 standard. Polycarboxylate based plasticizers synthesized at laboratory conditions were used at 1% by weight in both ordinary Portland cement mortar and geopolymer paste. Geopolymer samples were aged for 7 and 28 days at laboratory conditions while cement mortars were aged in water bath. The fluidity values of fresh mixtures were determined. The flexural strength and compressive strength tests were conducted at the ages of 7 and 28 days. The plasticizers had positive effects on cement mortars but unfavorable results on geopolymer. The use of plasticizer increased the fluidity and the strength values in mortars, on the contrary, admixtures caused decrease in the values of geopolymer samples. The highest compressive strength was obtained as 38.3 MPa for mortar sample aged for 28 days and was 15.3 MPa for geopolymer samples.

Özet

Chemical admixtures are generally used in ready mixed concrete production to improve and enhance the concrete properties. Polycarboxylate based superplasticizers are classified as third generation plasticizing admixtures which increase fluidity and workability without decreasing compressive strength. Geopolymers having many superior properties are alternative materials to ordinary Portland cement concrete. Geopolymers are environmentally friendly and sustainable materials because they can be synthesized from waste materials such as fly ash. In this experimental study, geopolymer pastes were produced by using fly ash, 10 M sodium hydroxide, sodium silicate solution and plasticizer. Cement mortars were produced according to TS EN 196-1 standard. Polycarboxylate based plasticizers synthesized at laboratory conditions were used at 1% by weight in both ordinary Portland cement mortar and geopolymer paste. Geopolymer samples were aged for 7 and 28 days at laboratory conditions while cement mortars were aged in water bath. The fluidity values of fresh mixtures were determined. The flexural strength and compressive strength tests were conducted at the ages of 7 and 28 days. The plasticizers had positive effects on cement mortars but unfavorable results on geopolymer. The use of plasticizer increased the fluidity and the strength values in mortars, on the contrary, admixtures caused decrease in the values of geopolymer samples. The highest compressive strength was obtained as 38.3 MPa for mortar sample aged for 28 days and was 15.3 MPa for geopolymer samples.

🔖

Cite This Article

Arıöz, E., Saraç, G., Arıöz, Ö., Koçkar, Ö. M. (2022). The Comparison of the Properties of Geopolymer Paste and Ordinary Portland Cement Mortar Produced Using Polycarboxylate Based Admixture. Avrupa Bilim ve Teknoloji Dergisi, Sayı: 34 Özel Sayı, 537–540. https://doi.org/10.31590/ejosat.1083318

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (15)

  1. Cagg, C. R. (2014). Cement and concrete as an engineering material: An historic appraisal and case study analysis. Engineering Failure Analysis, 40, 114 – 140. https://doi.org/10.1016/j.engfailanal.2014.02.004
  2. SinghN.B., KumarM. & Rai S. (2020). Geopolymer cement and concrete: Properties. Materials Today: Proceedings, 29, 743-748. https://doi.org/10.1016/j.matpr.2020.04.513
  3. Damme, H.V. (2018). Concrete material science: Past, present, and future innovations. Cement and Concrete Research, 112, 5-24. https://doi.org/10.1016/j.cemconres.2018.05.002
  4. Thamilselvi, P., Siva A., & D. Oyejobi. (2017). Geopolymer Concrete: Overview. International Journal of Advanced Research in Engineering and Technology, 8, 10-14.
  5. Pavithra P., Reddy M.S., Dinakar P., Rao B. H., Satpathy B.K. & Mohanty A.N. (2016). A mix design procedure for geopolymer concrete with fly ash. Journal of Cleaner Production, 133, 117-125. https://doi.org/10.1016/j.jclepro.2016.05.041
  6. Mehta A. & Siddique R. (2016). An overview of geopolymers derived from industrial by-products. Construction and Building Materials, 127, 183-198. https://doi.org/10.1016/j.conbuildmat.2016.09.136
  7. Li F., Chen D., Yang Z., Lu Y., Zhang H. & Li S. (2022). Effect of mixed fibers on fly ash-based geopolymer resistance against carbonation. Construction and Building Materials, 322, 126394. https://doi.org/10.1016/j.conbuildmat.2022.126394
  8. Degefu D.M., Liao Z., Berardi U. & Labbe G. (2022). The dependence of thermophysical and hygroscopic properties of macro-porous geopolymers on Si/Al. Journal of Non-Crystalline Solids, 582, 121432. https://doi.org/10.1016/j.jnoncrysol.2022.121432
  9. Podolsky Z., Liu J., Doh J.H., Guerrieri M. & Fragomeni S. (2021). State of the art on the application of waste materials in geopolymer concrete. Case Studies in Construction Materials, 15, e00687. https://doi.org/10.1016/j.cscm.2021.e00637
  10. Li S., Zhang J., Li Z., Gao Y. & Liu C. (2021). Feasibility study of red mud-blast furnace slag based geopolymeric grouting material: Effect of superplasticizers. Construction and Building Materials, 267, 120910. https://doi.org/10.1016/j.conbuildmat.2020.120910
  11. Mardani-Aghabaglou A., Tuyan M., Yılmaz G., Arıöz Ö. & Ramyar K. (2013). Effect of different types of superplasticizer on fresh, rheological and strength properties of self-consolidating concrete. Construction and Building Materials, 47, 1020-1025. https://doi.org/10.1016/j.conbuildmat.2013.05.105
  12. Wang C., Kayali O. & Liow J. (2021). The effectiveness and mechanisms of superplasticisers in dispersing class F fly ash pastes. Powder Technology, 392, 81-92. https://doi.org/10.1016/j.powtec.2021.06.054
  13. Kang S.H., Kwon M., Kwon Y. & Moon J. (2021). Effects of polycarboxylate ether (PCE)-based superplasticizer on the dissolution and subsequent hydration of calcium oxide (CaO). Cement and Concrete Research, 146, 106467. https://doi.org/10.1016/j.cemconres.2021.106467
  14. Ren J., Wang X., Xu S., Luo Q., Fang Y., Zhu J. & Xing F. (2021). Effects of polycarboxylate superplasticiser on hydration characteristics and hardened properties of cement blended with seawater. Construction and Building Materials, 304, 124660. https://doi.org/10.1016/j.conbuildmat.2021.124660
  15. Al-Shwaiter A., Awang H. & Khalaf M. A. (2021). The influence of superplasticiser on mechanical, transport and microstructure properties of foam concrete. Journal of King Saud University - Engineering Sciences, In Press, Corrected Proof, 2021. https://doi.org/10.1016/j.jksues.2021.02.010