AI InsightAccording to the results obtained, it has been determined that the addition of brick powder increased the mixing water necessity and extended the initial and final setting time of cement.
📌 3 Key Takeaways
Abstract
The use of brick powder in constructions dates back to very ancient civilizations. Generally, brick powder was mixed with lime and used in making mortar for masonry. In this study, the usability of brick powder as pozzolanic additive in cement mortar has been investigated. Cement is reduced 0 %, 10 %, 20 % and 30 % by weight and replaced with brick powder. For mechanical properties mortar samples with dimensions of 40 x 40 x 160 mm, were prepared. Mechanical properties of mortar samples were determined at the ages of 7, 28, 90 and 180 days. According to the results obtained, it has been determined that the addition of brick powder increased the mixing water necessity and extended the initial and final setting time of cement. The best results for compressive and flexural strengths have been obtained on the sample containing by 10 % brick powder
Özet
Tuğla ununun inşaatta kullanımı çok eski uygarlıklara dayanmaktadır. Genellikle tuğla unu kireçle karıştırılarak duvar harcı yapımında kullanılmıştır. Bu çalışmada, tuğla ununun çimento harcı içerisinde puzolanik katkı malzemesi olarak kullanılabilirliği araştırılmıştır. Çimento, ağırlıkça % 0, % 10, % 20 ve % 30’u oranlarında azaltılarak yerine tuğla unu ikame edilmiştir. Mekanik özellikler için 40 x 40 x 160 mm’ lik harç numuneleri hazırlanmıştır. 7, 28, 90 ve 180 günlük harç numunelerinin mekanik özellikleri tespit edilmiştir. Elde edilen sonuçlara göre; tuğla unu katkısının karışım suyu gereksinimini, priz başlama ve bitiş sürelerini artırdığı belirlenmiştir. Kontrol harcına göre, en iyi eğilme ve basınç dayanımı değerleri % 10 tuğla unu ikameli karışımdan elde edilmiştir.