AI Summary & Key Takeaways
AI InsightFor the soil briquets prepared with th enormal procedure it was found signifıcant (P<0.05) negative relation between modulus of rupture and shrinkage limit, but signifıcant (P<0.01) multiple relations between, modulus of rupture and clay content-organik matter content- briquet bulk density, and between modulus of rupture and clay conten briquet bulk density-aggregate stability.
📌 3 Key Takeaways
Özet
ÖZET : Bu çalışma, bazı yöntemsel faktörlerin yapay toprak briketlerinin kırılma değerinin ölçümü üzerine etkilerini ve bazı toprak özellikleri ile kırılma değeri arasındaki ilişkileri incelemek amacıyla yapılmıştır. Çalışmada, Atatürk Üniversitesi Ziraat Fakültesi Ziraat işletmesi arazisinin 12 farklı mahallinden 0-20 cm derinlikten alman toprak örnekleri kullanılmıştır. Kırılma değeri, normal prosedür ile hazırlanan briketlerde 83-515 mbar ve toprak macunu ile hazırlanan briketlerde ise 14322-27310 mbar olarak tespit edilmiştir ve macunlaştırma ile 36-285 kat artmıştır. Normal prosedür ve toprak macunu ile hazırlanan briketlerde, briket nem içeriği İle tınlt bir toprakta log kırılma değeri arasında ve killi tınlı bir toprakta ise kırılma değeri arasında doğrusal önemli (?<().01) negatif ilişkiler elde edilmiştir. Kırma kuvveti uygulanma hızının 400 g/da olması 800 gld'ya nazaran, ölçülen kırılma değerinde Önemli (P<0.05) bir azalmaya sebep olmuştur. Normal prosedür ile hazırlanan toprak briketlerinde kırılma değeri ile büzülme limiti arasında önemli (P<0.05) negatif bir ilişki elde edilmiştir. Fakat kırılma değeri ile kil içeriği organik madde içeriği-briket hacım ağırlığı ve kil içeriği-agregat stabilitesi-briket hacım ağırlığı arasında P<0.01 düzeyinde önemli çoklu ilişkiler bulunmuştur. Macunla hazırlanan toprak briketlerinde ise, kırılma değeri ile kil içeriği, mil içeriği, likit limit, plastik limit, plastiklik indeksi, büzülme indeksi, doğrusal büzülme, hacımsal büzülme arasında önemli (P<0.05) pozitif ilişkiler ve plastik limit/pF 2 nemi oranı arasında önemli (P <0.05) negatif bir ilişki elde edilmiştir. EFFECTS OF SOME METHODICAL FACTORS AND SOİL PROPERTİES ON THE MODULUS OF RUPTURE OF SOİLS SUMMARY : The purpose of this study was to determine the effects of some methodical factors on the measurement of the modulus of rupture of artificial soil briquets and the relations betvveen some soil properties and modulus of rupture. Soil samples taken from the 0-20 cm depth of 12 different sites on the from of the Agricultural Faculty of Atatürk University Erzurum w ere used in the work. Modulus of rupture values were obtained between 83 and 515 mbar for the briquets prepared with the normal procedure and between 14322 and 27310 mbar for the briguets prepared with the puddled soil and increased as much as 36 to 285 times upon puddling. Linear negative relations were found between the moisture content of the briquets and logarithm of the modulus of rupture value for a loam soil and between the moisture content of the briquets and the modulus of rupture value for a clay loam soil. With 400 g/d application rate of breaking force it was obtained signifıcant (P<0J)5) decrease in the modulus of rupture measured with compared to 800 gld. For the soil briquets prepared with th enormal procedure it was found signifıcant (P<0.05) negative relation between modulus of rupture and shrinkage limit, but signifıcant (P<0.01) multiple relations between, modulus of rupture and clay content-organik matter content- briquet bulk density, and between modulus of rupture and clay conten briquet bulk density-aggregate stability. For the briquets prepared with the puddled soil it was found signifıcant positive relations between modulus of rupture and clay cocntent, between modulus of rupture and sil t conten, between modulus of rupture and liquİd limit, between modulus of rupture and plastic limit, between modulus of rupture and plasticityi index, between modulus of rupture and shrinkage inde, between modulus of rupture and linear shrinkage, between modulus of rupture and volumetric shrinkage, but significant negative relation betvveen modulus of rupture and the ratio of plastic limit pF 2 moisture content.