Fracture behavior of bolted joints in composites repaired with patch: 3D numerical approach

Yama ile tamir edilmiş pim bağlantılı kompozitlerin kırılma davranışı: Üç boyutlu sayısal yaklaşım

Yunus Gündüz
Mete Onur Kaman
Pages
643–649
Publication Date
2018-08-17
DOI
—
🏛️Bibliographic metadata and full text access for this article are provided via DergiPark.
DergiPark Record ↗
✨

AI Summary & Key Takeaways

AI Insight
⚡ TL;DR(Too Long; Didn't Read)

Yama malzemesi değişiminin şiddet faktörü üzerinde üzerindeki etkisi büyük pim çaplarında artmıştır.

📌 3 Key Takeaways

🎯
Objective & Hypothesis:Normal 0 false false false TR X-NONE X-NONE /* Style Definitions */ table.MsoNormalTable {mso-style-name:"Normal Tablo"; mso-tstyle-rowband-size:0; mso-tstyle-colband-size:0; mso-style-noshow:yes; mso-style-priority:99; mso-style-parent:""; mso-padding-alt:0cm 5.4pt 0cm 5.4pt; mso-para-margin-top:0cm; mso-para-margin-right:0cm; mso-para-margin-bottom:10.0pt; mso-para-margin-left:0cm; line-height:115%; mso-pagination:widow-orphan; font-size:11.0pt; font-family:"Calibri",sans-serif; mso-ascii-font-family:Calibri; mso-ascii-theme-font:minor-latin; mso-hansi-font-family:Calibri; mso-hansi-theme-font:minor-latin; mso-bidi-font-family:"Times New Roman"; mso-bidi-theme-font:minor-bidi; mso-ansi-language:TR;} Bu çalışmada, bir yüzü kompozit yamalı ve pim delikli kompozit levhaların kırılma davranışı sayısal olarak araştırılmıştır.
📊
Key Findings & Data:Levha ve yama malzemesi, pim çapı ve yapıştırıcı özellikleri gibi parametrelerin değişiminin çatlak ucu gerilme şiddet faktörü üzerindeki etkileri araştırılmıştır.
💡
Conclusion & Impact:Yama malzemesi değişiminin şiddet faktörü üzerinde üzerindeki etkisi büyük pim çaplarında artmıştır.
🔬Design:Modeling & Simulation
📍Scope:Comprehensive Sample
⚙️Variables:Gerilme şiddet faktörü · Ortotropik · Tamir

Özet

Normal 0 false false false TR X-NONE X-NONE /* Style Definitions */ table.MsoNormalTable {mso-style-name:"Normal Tablo"; mso-tstyle-rowband-size:0; mso-tstyle-colband-size:0; mso-style-noshow:yes; mso-style-priority:99; mso-style-parent:""; mso-padding-alt:0cm 5.4pt 0cm 5.4pt; mso-para-margin-top:0cm; mso-para-margin-right:0cm; mso-para-margin-bottom:10.0pt; mso-para-margin-left:0cm; line-height:115%; mso-pagination:widow-orphan; font-size:11.0pt; font-family:"Calibri",sans-serif; mso-ascii-font-family:Calibri; mso-ascii-theme-font:minor-latin; mso-hansi-font-family:Calibri; mso-hansi-theme-font:minor-latin; mso-bidi-font-family:"Times New Roman"; mso-bidi-theme-font:minor-bidi; mso-ansi-language:TR;} Bu çalışmada, bir yüzü kompozit yamalı ve pim delikli kompozit levhaların kırılma davranışı sayısal olarak araştırılmıştır. Levha ve yama malzemesi, pim çapı ve yapıştırıcı özellikleri gibi parametrelerin değişiminin çatlak ucu gerilme şiddet faktörü üzerindeki etkileri araştırılmıştır. Çözümde; yama ile tamir edilmiş levha üç boyutlu olarak modellenmiş ve pim deliği kenarındaki çatlak ucu yer değiştirmeleri sonlu elemanlar yöntemi ile bulunmuştur. Gerilme şiddet faktörü; homojen ortotropik malzemeler için üç boyutlu çatlak problemlerine uygulanabilen DCM ( Displacement Correlation Method ) ile elde edilmiştir ve sonuçlar grafikler halinde sunulmuştur. Pim deliği merkezinden aynı uzaklıktaki çatlak uçları için, büyük delik çaplarının, büyük çatlak uzunluğuna göre gerilme şiddet faktörü üzerinde daha etkili bir parametre olduğu görülmüştür. Yama malzemesi değişiminin şiddet faktörü üzerinde üzerindeki etkisi büyük pim çaplarında artmıştır.

🔖

Cite This Article

Gündüz, Y., Kaman, M. O. (2018). Fracture behavior of bolted joints in composites repaired with patch: 3D numerical approach. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, Cilt: 24 Sayı: 4, 643–649. https://ajindex.com/articles/1058744

📄 Full Text PDF Viewer

📄

PDF görüntüleyici hazırlanıyor...

References (32)

  1. Dano ML, Gendron G, Picard A. “Stress and failure analysis of mechanically fastened joints in composite laminates”. Composite Structures, 50(3), 287-296, 2000.
  2. Ayatollahi MR, Hashemi R. “Mixed mode fracture in an inclined center crack repaired by composite patching”. Composite Structures, 81(2), 264-273, 2007.
  3. Bouiadjra BB, Belhouari M, Serier B. “Computation of the stress intensity factors for repaired cracks with bonded composite patch in mod I and mixed mode”. Composite Structures, 56(4), 401-406, 2002.
  4. Seo DC, Lee JJ. “Fatigue crack growth behavior of cracked aluminum plate repaired with composite patch”. Composite Structures, 57(1-4), 323-330, 2002.
  5. Schubbe JJ, Mall S. “Investigation of a cracked thick aluminum panel repaired with a bonded composite patch”. Engineering Fracture Mechanics, 63(3), 305-323, 1999.
  6. Emdad R, Al-Mahaidi R. “Effect of prestressed CFRP patches on crack growth of centre-notched steel plates”. Composite Structures, 123, 109-122, 2015.
  7. Reddy S, Jaswanthsai V, Madhavann M, Kumar V. “Notch stress intensity factor for center cracked plates with crack stop hole strengthened using CFRP: A numerical study”. Thin-Walled Structures, 98(B), 252-262, 2016.
  8. Srilakshmi R, Ramji M, Chinthapenta V. “Fatigue crack growth study of CFRP patch repaired Al 2014-T6 panel having an inclined center crack using FEA and DIC”. Engineering Fracture Mechanics, 134, 182-201, 2015.
  9. Errouane H, Sereir Z, Chateauneuf A. “Numerical model for optimal design of composite patch repair of cracked aluminum plates under tension”. International Journal of Adhesion and Adhesives, 49, 64-72, 2014.
  10. Turan K, Kaman MO, Gur M. “Progressive failure analysis of laminated composite plates with two serial pinned joints”. Mechanics of Advanced Materials and Structures, 22(10), 839-849, 2015.
  11. Liu X, Wang G. “Progressive failure analysis of bonded composite repairs”. Composite Structures, 81(3), 331-340, 2007.
  12. Okutan B, Karakuzu R. “The strength of pinned joints in laminated composites”. Composites Science and Technology, 63(6), 893-905, 2003.
  13. Atas A, Arslan N, Sen F. “Failure analysis of laminated composite plates with two parallel pin-loaded holes”. Journal of Reinforced Plastics and Composites, 28(10), 1265-1276, 2009.
  14. Madani K, Touzain S, Feaugas X, Cohendouz S, Ratwani M. “Experimental and numerical study of repair techniques for panels with geometrical discontinuities”. Computational Materials Science, 48(1), 83-93, 2010.
  15. Ahmad H, Crocombe AD, Smith PA. “Strength prediction in CFRP woven laminate bolted double-lap joints under quasi-static loading using XFEM”. Composites: Part A, 56 192-202, 2014.
  16. Abd-Elhady AA, Sallam HEDM. “Crack sensitivity of bolted metallic and polymeric joints”. Engineering Fracture Mechanics, 147, 55–71, 2015.
  17. Liging W, Bingzheng G. “Numerical computation of stress intensity factor for bolt-hole corner crack in mechanical joints”, Chinese Journal of Aeronautics, 21(5), 411-416, 2008.
  18. Fawaz AS, Anderson B. “Accurate stress intensity factor solutions for corner cracks at a hole”, Engineering Fracture Mechanics, 71, 1235-1254, 2004.
  19. Horng LT, Ju HS. “Behaviors of a single crack in multiple bolted joints”, International Journal of Solids and Structures, 36(27), 4055-4070, 1999.
  20. Wanga W, Ransa C, Zhangb Z, Benedictus R. “Prediction methodology for fatigue crack growth behaviour in fibre metal laminates subjected to tension and pin loading”. Composite Structures, 182(15), 176-182, 2017.
  21. Kabeel AM, Maimi P, Gonzalez EV, Gascons N. “Net-tension strength of double-lap joints under bearing-bypass loading conditions using the cohesive zone mode”. Composite Structures, 119, 443-451, 2015.
  22. ANSYS, 13.0, (Academic Teaching Introductory) Command References and Gui.
  23. Arman Y, Zor M, Aksoy S. “Determination of critical delamination diameter of laminated composite plates under buckling loads”. Composites Science and Technology, 66(15), 2945-2953, 2006.
  24. Okafor C, Bhogapurapu H. “Design and analysis of adhesively bonded thick composite patch repair of corrosion grind-out and cracks on 2024 T3 clad aluminum aging aircraft structures”. Composite Structures, 6(1-2), 138-150, 2006.
  25. Toudeshkya HH, Ghaffaria MA, Mohammadib B. “Fatigue propagation of induced cracks by stiffeners in repaired panels with composite patches”. Procedia Engineering, 10, 3285-3290, 2011.
  26. Gu L, Kasavajhala ARM, Zhao S. “Finite element analysis of cracks in aging aircraft structures with bonded composite-patch repairs”. Composites: Part B, 42(3), 505-510, 2011.
  27. Ozkan U, Kaya AC, Loghin A, Ayhan A, Nied HF. “Fracture analysis of cracks in anisotropic materials using 3DFAS and ANSYS”, ASME Applied Mechanics Division, Proceedings of IMECE 2006, Chicago, Illinois, USA, 5-10 November 2006.
  28. Kaman MO, Cetişli F. “Yama ile tamir edilmiş kenar çatlak içeren kompozit levha probleminin sayısal analizi”. 9. Uluslararası Kırılma Konferansı, Yıldız Teknik Üniversitesi, İstanbul, Türkiye, 19-21 Ekim 2011.
  29. Gündüz Y. Yama ile Tamir Edilmiş Çatlak İçeren Pim Bağlantılı Kompozitlerde Kırılma Davranışının Sayısal Analizi. Yüksek Lisans Tezi, Fırat Üniversitesi, Elazığ, Türkiye, 2013.
  30. Turaga VRS, Ripudaman S. “Modeling of patch repairs to a thin cracked sheet”. Engineering Fracture Mechanics, 62(2-3), 267-89, 1999.
  31. Kaman MO, Gündüz Y, Turan K. “Kompozit yama ile tamir edilmiş pim delikli levhalarda çatlak problemi”. I. Ulusal Ege Kompozit Malzemeler Sempozyumu, İzmir, Türkiye, 17-19 Kasım, 2011.
  32. Kaya AC, Erdogan F. “Stress intensity factors and COD in an orthotropic strip”. International Journal of Fracture, 16(2), 171-190, 1980.