In this study, the wear behavior of special brass produced from centrifugal cast method and green mould cast method were investigated under dry sliding conditions by pin on disc. Ferritic ductile iron disc has been used as counter abrader. Wear tests were carried out using a pin-on-disc type apparatus, at a linear sliding speed of 0.3 m s-1, under the loads of 10 N, 20 N and 30 N and sliding distance of 600 m, in ambient air at room temperature, dry sliding conditions. Although the centrifugal cast method specimen had higher hardness than the green mould cast specimen, with applied load increasing both two methods produced specimens wear loses decreased.
Özet
Bu çalışmada, geleneksel kum kalıba döküm yöntemi ve merkezkaç döküm yöntemiyle üretilen CuZn34Al2 özel pirinç malzemenin aşınma davranışı araştırılmıştır. Karşı aşındırıcı olarak ferritik küresel grafitli dökme demir disk kullanılmıştır. Aşınma testleri disk üzerinde pim cihazında, 0.3 m s-1 kayma hızında, 10,20 ve 30 N yük altında ve 600m kayma mesafesinde, oda sıcaklığında, kuru kayma şartlarında gerçekleştirilmiştir. Sonuç olarak, savurma döküm yöntemiyle üretilen numunenin sertliği, kum kalıba döküm yöntemiyle üretilen numuneden daha yüksek olmasına rağmen, uygulanan yükün artmasıyla birlikte her iki döküm yöntemiyle üretilen numunelerin aşınma kaybı azalmıştır.