THE EFFECTS OF VARIOUS MIXING VEHICLES ON PUSH OUT BOND STRENGTH OF PROROOT MTA

FARKLI TAŞIYICILARIN PROROOT MTA’NIN PUSH-OUT BAĞLANMA DAYANIMINA ETKİSİ

AYHAN EYMİRLİ,EMEL UZUNOĞLU ÖZYÜREK,MEHMET ÖZGÜR UYANIK,ZEYNEL EMRE NAGAŞ

Sayfa
74–79
DOI
—

Özet

Background and Aim: The purpose of this study was to assess the effect of different mixing vehicles on the push-out bond strength of ProRoot MTA. Materials and Methods: Two hundred and ten 1-mm-thick root slices were randomly assigned into 7 groups with respect to the mixing vehicles (n=30/group): 1: (control group); distilled water, 2: 2% chlorhexidine digluconate; 3: articaine; 4: 5,25% sodium hypochlorite; 5: propylene glycol; 6: antiwashout gel; and 7: calcium chloride. In each group, test liquid was mixed with ProRoot MTA. Push-out bond strength test was performed and the data were analyzed statistically using one-way analysis of variance (ANOVA) and Tukey’s post-hoc tests (p=0.05). Results: Mean push-out values of viscous mixing vehicles such as calcium chloride, antiwashout gel and propylene glycol groups were similar (p>0.05) and significantly greater from those of other groups (p<0.05). Conclusion: Viscous mixing vehicles significantly increase the push-out bond strength of ProRoot MTA.

Abstract

Amaç: Bu çalışmanın amacı farklı taşıyıcıların ProRoot MTA’nın push-out bağlanma dayanımına etkisinin değerlendirilmesidir. Gereç ve Yöntem: 1 mm kalınlığında 210 adet kesit taşıyıcılarına göre 7 gruba ayrılmıştır (n=30). 1. Grup(kontrol grubu): distile su, 2: 2% klorheksidin diglukonat; 3: articaine; 4: 5,25% sodyum hipoklorit; 5: propilen glikol; 6: antiwashout jel; ve 7: kalsiyum klorit. Her gruptaki test likidi ProRoot MTA ile karıştırıldı. Push-out bağlanma dayanımı testleri yapıldı ve elde edilen veriler tek yönlü varyans analizi (ANOVA) ve post-hoc Tukey testleri kullanılarak istatistiksel olarak analiz edildi(p=0.05). Bulgular: Antiwashout jel, kalsiyum klorit ve propilen glikol gruplarının ortalama push-out değerleri birbirleriyle benzer bulunurken(p>0.05) kalan diğer gruplardan yüksek bulunmuştur(p<0.05) Sonuç: Visköz taşıyıcılar ProRoot MTA’nın push-out bağlanma dayanımını artırmaktadır.